σU
MPa
σY
MPa
ϵL
ψ
KU
J

1.6513 (28NiCrMo4)

Classification

Country	Section	Category
Country	Section	Category
Germany	Structural, Pressure Vessel and Engineering Steels	Cr-Ni-Mo with Mo < 0.4% + Ni < 0.2%

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %
	95.69–97.11	0.15–0.4	0.3–0.6	1–1.3	1–1.3	< 0.035	0.24–0.34	< 0.035	0.2–0.3

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KU$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KU$ , $J$	Treatment
		101–160			740–930	> 590	< 13	< 60	< 20	After hardening and tempering

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
		soft, annealing	< 217

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KU$	$J$	Impact energy