12H21N5G2SAL
for producing castings for various industrial applications. Steel austenitic-ferritic class.
for producing castings for various industrial applications. Steel austenitic-ferritic class.
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % | N, % |
---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % | N, % |
GOST 977-88 | 68.1–75.9 | < 1.5 | < 2 | 20–22 | 4–6 | < 0.04 | < 0.12 | < 0.04 | 0.1–0.2 |
Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\sigma_{Y}$$, $$MPa$$ | $$\psi$$, % | $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ | d5, % | Treatment |
---|---|---|---|---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\sigma_{Y}$$, $$MPa$$ | $$\psi$$, % | $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ | d5, % | Treatment |
Castings | GOST 977-88 | 657 | 334 | 20 | 245 | 18 |
Standard | Description |
---|---|
Standard | Description |
GOST 977-88 |
Parameter | Units of measurement | Description |
---|---|---|
Parameter | Units of measurement | Description |
d5 | % | Elongation at break |
$$\sigma_{Y}$$ | $$MPa$$ | Yield strength |
$$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
$$\psi$$ | % | Reduction in cross section on fracture |
$$KCU\cdot 10^{3}$$ | $$\frac{J}{m^2}$$ | Impact toughness |