32G2Rps

Weldability without restrictions.

manufacture of valves class A-III (A400), designed for reinforcement of ordinary and prestressed concrete structures

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Low alloy structural steel for welded structures

Chemical composition

Standard Fe, % Si, % B, % Mn, % Cr, % Cu, % Ni, % Al, % P, % C, % S, %
GOST 5781-82 96.693–98.418 < 0.17 0.001–0.007 1.3–1.75 < 0.3 < 0.3 < 0.3 0.001–0.015 < 0.045 0.28–0.37 < 0.05

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Fittings GOST 5781-82 590 390 14

Technological Properties

Weldability
no limits

Analogues

Germany USA
BSt 420 S E295

Standards

Standard Description
GOST 5781-82

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
B % Bor
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
Al % Aluminium
P % Phosphorus
C % Carbon
S % Sulfur

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures