60G

Substitute: 65G

Flat and round springs, springs, spring rings and other spring-type parts, which require high elastic properties and wear resistance; bandages, brake drums and bands, brackets, bushings and other parts of general and heavy engineering.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Spring-spring structural steel

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % P, % C, % S, %
GOST 14959-79 97.21–98.56 0.17–0.37 0.7–1 < 0.25 < 0.2 < 0.25 < 0.035 0.57–0.65 < 0.035

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$
20 2.04 7810
100 11.6 0.483
200 11.9 0.487
300 12.9
400 13.8 0.529
600 14.6 0.575

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\psi$$, % d5, % Treatment
Hire GOST 14959-79 heat-treated 980 785 30 8 Tempering 830 ° C, oil, leave 470 ° C
The tape is hardcore. GOST 2283-79 cold-work 740–1180
The tape is annealed. GOST 2283-79 annealing 640–740 10–15

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy GOST 14959-79 raw 285
Hire GOST 14959-79 heat-treated 241
The plates GOST 1577-93 normalization, fat 269
The plates GOST 1577-93 annealing, fat 229

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
Not applicable for welded structures insensitive inclined

Critical point temperatures

Ac1, K Ac3(Acm), K Ar3(Arcm), K Ar1, K Mn, K
726 765 741 689 270

Analogues

USA Germany European Union
G15610 1.0601 (C60) 1CS60

Standards

Standard Description
GOST 14959-79

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)

Description of mechanical properties

Parameter Units of measurement Description
d5 % Elongation at break
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\psi$$ % Reduction in cross section on fracture

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter Units of measurement Description
Ac1 K
Ac3(Acm) K
Ar3(Arcm) K
Ar1 K
Mn K