Aluminum alloy AK8M3ch (VAL8)
Chemical composition
Al Aluminum Rest Be Beryllium 0.05 — 0.25 B Boron 0.005 — 0.100 Fe Iron <0.4 Cd Cadmium <0.15 Si Silicon 7.0 — 8.5 Mg Magnesium 0.25 — 0.50 Cu Copper 2.5 — 3.5 Ni Nickel <0.02 Sn Tin <0.02 Pb Lead <0.02 Ti Titanium 0.10 — 0.25 Zn Zinc 0.5 — 1.0 Zr Zirconium <0.15 Ot Total impurities <0.6
Casting methods:
Z — sand casting
B — Lost wax casting
K — chill casting
D — injection molding
Mark designation:
h — clean
bees — high purity
och — high purity
l — casting alloys
c — selective
Lack of B is allowed provided that the level of mechanical characteristics is ensured.
Analogs in Germany
GK-AlSi9Cu3 DIN 1725 Part 2
3.2163.02 DIN 1725 Part 2
G-AlSi9Cu3 DIN 1725 Part 2
3.2163.01 DIN 1725 Part 2
EN AC-46200 DIN EN 1706: 2013
EN AC-AlSi8Cu3 DIN EN 1706: 2013
EN AC-46200 DIN EN 1706: 2019
EN AC-AlSi8Cu3 DIN EN 1706: 2019
AlSi8Cu3 TGL 6556/02
AlSi8Cu3 TGL 6556/02
226 VDS
Analogs in the USA
SC 84B
SC 84A
SC 84A
A380.0 AA
A380.1 AA
A380.1-N AA
A380.1-S AA
A380.1-C AA
A380.1-P AA
4291 AMS
EN AC-46200 ASME SB / EN 1706
EN AC-AlSi8Cu3 ASME SB / EN 1706
B 179 (A380.1) ASTM B179
B 179 (A380.1-N) ASTM B179
B 179 (A380.1-S) ASTM B179
B 179 (A380.1-C) ASTM B179
B 179 (A380.1-P) ASTM B179
B 275 (A 13800) ASTM B275
B 275 (A 13801) ASTM B275
B 85 (A380.0) ASTM B85
A380.1 QQ A-371F
J452 (306) SAE J452
A13800 UNS
A13801 UNS
Analogs in Russia
VAL8 GOST 1583−93
AL8 GOST 2171−90
AK8M3ch GOST R 55375−12
VAL8 GOST R 55375−12
For the manufacture of power and sealed parts operating up to 250 degrees., Manufactured by injection molding. Technical requirements GOST 1583−93 Cast aluminum alloys. Technical conditions GOST R 55375−12 Primary aluminum and alloys based on it. Stamps
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Aluminum, aluminum alloys | Foundry aluminum alloys |
Chemical composition
| Standard | Fe, % | Si, % | B, % | Be, % | Mg, % | Ti, % | Cu, % | Zn, % | Zr, % | Al, % | Cd, % |
|---|---|---|---|---|---|---|---|---|---|---|---|
| GOST 1583-93 | < 0.4 | 7–8.5 | 0.005–0.1 | 0.05–0.25 | 0.2–0.45 | 0.1–0.25 | 2.5–3.5 | 0.5–1 | < 0.15 | 85.4–89.65 | < 0.15 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | δ, % | Treatment |
|---|---|---|---|---|---|---|---|
| Casting | GOST 1583-93 | 215–392 | 1–5 |
Standards
| Standard | Description |
|---|---|
| GOST 1583-93 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| B | % | Bor |
| Be | % | Beryllium |
| Mg | % | Magnesium |
| Ti | % | Titan |
| Cu | % | Copper |
| Zn | % | Zinc |
| Zr | % | Zirconium |
| Al | % | Aluminium |
| Cd | % | Cadmium |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| δ | % | Elongation after rupture |
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |