Amg1 (1510)

For the manufacture of semi-finished products (sheets, tapes, strips, plates, profiles, panels, pipes, wire, stampings and forgings) by hot or cold deformation; corrosion resistance high

Classification

Country Section Category
CIS, Russia, Ukraine Aluminum, aluminum alloys Wrought Aluminum Alloys

Chemical composition

Standard Fe, % Si, % Mg, % Mn, % Cr, % Cu, % Zn, % Al, %
GOST 4784-97 < 0.7 < 0.3 0.5–1.1 < 0.2 < 0.1 < 0.2 < 0.25 97.15–99.5

Information on suppliers

Physical characteristics

Temperature, °C $$\rho$$, $$\frac{kg}{m^3}$$
20 2690

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Trumpet annealing 120–175 10
Trumpet cold-work 165

Technological Properties

Weldability
no limits

Analogues

Germany USA
3.3315 AA5005

Standards

Standard Description
GOST 4784-97
GOST 9498-79 GOST 9498 - 79
OST 1-92014 - 90

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mg % Magnesium
Mn % Manganese
Cr % Chrome
Cu % Copper
Zn % Zinc
Al % Aluminium

Description of physical characteristics

Parameter Units of measurement Description
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures