L70
radiator tapes, strips, pipes, heat exchangers; musical instruments; Details obtained by deep drawing;
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Brass (copper-zinc alloy) |
Brass, pressure treated |
Chemical composition
| Standard |
Fe, % |
Bi, % |
Cu, % |
Zn, % |
Sb, % |
Pb, % |
P, % |
|---|
| GOST 15527-2004 |
< 0.07 |
< 0.002 |
69–71 |
28.67–30.8 |
< 0.002 |
< 0.05 |
< 0.005 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$E\cdot 10^{9}$$, $$MPa$$ |
$$\alpha\cdot 10^{6}$$, $$K^{-1}$$ |
$$\varkappa$$, $$\frac{W}{m\cdot K}$$ |
$$\rho$$, $$\frac{kg}{m^3}$$ |
$$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ |
$$R\cdot 10^{-6}$$, $$\Omega\cdot m$$ |
|---|
| 20 |
115 |
|
121.4 |
8500 |
|
0.069 |
| 100 |
|
18.9 |
|
|
0.3768 |
|
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
| Sheet |
|
|
|
soft |
270–360 |
|
40 |
|
| Sheet |
|
|
|
solid |
430 |
|
10 |
|
| Trumpet |
|
|
|
half-firm, solid |
340 |
130 |
35 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Sheet |
|
soft |
0–0 |
| Sheet |
|
solid |
0–0 |
Casting and technological parameters
| melting point, °C |
Hot working temperature, °C |
annealing temperature, °C |
|---|
| 950 |
700–850 |
550–650 |
Analogues
| USA |
Germany |
|---|
| C26000 |
2.0265 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Bi |
% |
Bismuth |
| Cu |
% |
Copper |
| Zn |
% |
Zinc |
| Sb |
% |
Antimony |
| Pb |
% |
Lead |
| P |
% |
Phosphorus |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| $$E\cdot 10^{9}$$ |
$$MPa$$ |
Elastic modulus |
| $$\alpha\cdot 10^{6}$$ |
$$K^{-1}$$ |
Coefficient of thermal (linear) expansion (range 20°C–T) |
| $$\varkappa$$ |
$$\frac{W}{m\cdot K}$$ |
Coefficient of thermal conductivity (the heat capacity of the material) |
| $$\rho$$ |
$$\frac{kg}{m^3}$$ |
The density of the material |
| $$c\cdot 10^{-3}$$ |
$$\frac{J}{kg\cdot K}$$ |
The specific heat of the material (range 20°C–T) |
| $$R\cdot 10^{-6}$$ |
$$\Omega\cdot m$$ |
Electrical resistivity |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
Description of the casting and technological parameters
| Parameter |
Units of measurement |
Description |
| melting point |
°C |
The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa |
| Hot working temperature |
°C |
The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment |
| annealing temperature |
°C |
The temperature at which the processes return recrystallization and homogenization of the metal to reduce its hardness for subsequent machining |