SCH15
for the manufacture of castings
for the manufacture of castings
Standard | Fe, % | Si, % | Mn, % | P, % | C, % | S, % |
---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | P, % | C, % | S, % |
GOST 1412-85 | 92.75–94 | 2–2.4 | 0.5–0.8 | < 0.2 | 3.5–3.7 | < 0.15 |
Temperature, °C | E\cdot 10^{9}, MPa | \alpha\cdot 10^{6}, K^{-1} | \varkappa, \frac{W}{m\cdot K} | \rho, \frac{kg}{m^3} | c\cdot 10^{-3}, \frac{J}{kg\cdot K} |
---|---|---|---|---|---|
Temperature, °C | E\cdot 10^{9}, MPa | \alpha\cdot 10^{6}, K^{-1} | \varkappa, \frac{W}{m\cdot K} | \rho, \frac{kg}{m^3} | c\cdot 10^{-3}, \frac{J}{kg\cdot K} |
20 | 90 | 59 | 7000 | ||
100 | 9 | 0.46 |
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | Treatment |
---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | Treatment |
Casting | GOST 1412-85 | 150 |
Rolling | Standard | Classifiers | Value, HBW |
---|---|---|---|
Rolling | Standard | Classifiers | Value, HBW |
GOST 1412-85 | 130–241 |
Standard | Description |
---|---|
Standard | Description |
GOST 1412-85 |
Parameter | Units of measurement | Description |
---|---|---|
Parameter | Units of measurement | Description |
E\cdot 10^{9} | MPa | Elastic modulus |
\alpha\cdot 10^{6} | K^{-1} | Coefficient of thermal (linear) expansion (range 20°C–T) |
\varkappa | \frac{W}{m\cdot K} | Coefficient of thermal conductivity (the heat capacity of the material) |
\rho | \frac{kg}{m^3} | The density of the material |
c\cdot 10^{-3} | \frac{J}{kg\cdot K} | The specific heat of the material (range 20°C–T) |