St2sp (VSt2sp)

non-critical items requiring higher ductility or deep-drawing; malanagruzhennye elements of welded structures operating at constant load and at positive temperatures

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Carbonaceous structural steel of ordinary quality

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % As, % P, % C, % S, % N, %
GOST 380-2005 97.972–99.51 0.15–0.3 0.25–0.5 < 0.3 < 0.3 < 0.3 < 0.08 < 0.04 0.09–0.15 < 0.05 < 0.008

Information on suppliers

Physical characteristics

Temperature, °C $$\rho$$, $$\frac{kg}{m^3}$$
20 7850

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % $$\psi$$, % Treatment
Trumpet GOST 8696-74 334 225 24
Trumpet GOST 10705-80 333 206 24
Hire GOST 535-2005 335–430 195–225 29–32
The plates GOST 14637-89 330–430 195–225 29–32
Rod GOST 30136-95 420–470 60

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy 1160

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
no limits not sensitive not inclined

Analogues

USA Germany
K02502 1.0032 (St 34-2)

Standards

Standard Description
GOST 380-2005

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
As % Arsenic
P % Phosphorus
C % Carbon
S % Sulfur
N % Nitrogen

Description of physical characteristics

Parameter Units of measurement Description
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\psi$$ % Reduction in cross section on fracture

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures