St-08HM
Welding cold drawn wire of stainless steel, for welding (welding) and the manufacture of electrodes
Welding cold drawn wire of stainless steel, for welding (welding) and the manufacture of electrodes
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % | Mo, % | N, % |
---|---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % | Mo, % | N, % |
GOST 2246-70 | 96.733–98.07 | 0.12–0.3 | 0.35–0.6 | 0.9–1.2 | < 0.3 | < 0.03 | 0.06–0.1 | < 0.025 | 0.5–0.7 | < 0.012 |
Property |
---|
Property |
Note Fluctuations in the tensile strength in one coil of wire with a diameter of more than 1.4 mm should not exceed 90 N / mm2. |
For welding Diameter: 0.3 - 0.5 mm; Temporary resistance: 890 - 1390 MP |
Diameter: 0.8 - 1.5 mm; Temporary resistance: 890 - 1340 MPa |
Diameter: 1.6mm; Temporary resistance: 890 - 1290 MPa |
Diameter: 2mm; Temporary resistance: 790 - 1190 MPa |
Diameter:> 2 mm; Temporary resistance: 690 - 1040 MPa |
For the manufacture of electrodes Diameter: 1.6 mm; Temporary resistance: 690 - 990 MPa |
Diameter: 2mm; Temporary resistance: 690 - 990 MPa |
Diameter:> 2 mm; Temporary resistance: 640 - 940 MPa |
Density: 7.86 g / cm3 |
Standard | Description |
---|---|
Standard | Description |
GOST 2246-70 | |
OST 26-291-94 | |
TU 14-15-345-94 | |
TU 14-15-346-94 | |
TU 14-4-1877-2004 | |
TU У 27.1-4-548-2003 |