1.0033 (E155)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Base Steels |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
P, % |
C, % |
S, % |
|---|
| DIN EN 10296-1:2003 |
> 98.75 |
< 0.35 |
< 0.7 |
< 0.045 |
< 0.11 |
< 0.045 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
|
|
|
|
raw |
290 |
175 |
15 |
|
|
|
|
|
annealing, soft |
260 |
|
28 |
|
|
|
|
|
normalization |
270–410 |
155 |
|
|
|
|
|
|
solid, cold drawn |
400 |
|
6 |
|
|
|
|
|
soft, cold drawn |
350 |
|
10 |
|
|
|
|
|
stress relief, cold drawn |
350 |
245 |
18 |
|
Properties
| Property |
|---|
| According to EN 10296-1 note elongation: results from the longitudinal samples must be 2% below the results for the transverse samples |
| According to EN 10296-1 +U +NW yield strength: > 175 MPa |
| According to EN 10296-1 +U +NW tensile strength: > 290 MPa |
| According to EN 10296-1 +U +NW elongation: > 15 % |
| According to EN 10296-1 +A tensile strength: > 260 MPa |
| According to EN 10296-1 +A elongation: > 28 % |
| According to EN 10296-1 +N yield strength: > 155 MPa |
| According to EN 10296-1 +N tensile strength: > 270 MPa |
| According to EN 10296-1 +N elongation: > 28 % |
| Weldability In ISO/TR 20172 Group: 1.1 |
| Density: 7.85 g / cm3 |
Analogues
| Germany |
CIS, Russia, Ukraine |
|---|
| E155 |
E155 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |