1.0116 (S235J2G3)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Quality Steel (General Structural Steels with Rm < 500 MPa) |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
Al, % |
P, % |
C, % |
S, % |
Mo, % |
|---|
| DIN EN 10025:1990 |
97.11–99.98 |
< 0.55 |
< 1.4 |
< 0.3 |
< 0.3 |
> 0.02 |
< 0.035 |
< 0.17 |
< 0.035 |
< 0.08 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$R_{eH}$$, $$MPa$$ |
Treatment |
|---|
|
|
< 100 |
|
normalization |
340 |
24 |
215 |
|
|
|
100–250 |
|
normalization |
340 |
23 |
175 |
|
|
|
250–500 |
|
normalization |
340 |
23 |
165 |
|
Properties
| Property |
|---|
| Weldability In ISO/TR 20172 Group: 1.1 |
| Density: 7.86 g/cm3 |
Analogues
| CIS, Russia, Ukraine |
Germany |
USA |
|---|
| 16D |
St 37-3 N |
260W |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Mo |
% |
Molybdenum |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$R_{eH}$$ |
$$MPa$$ |
Upper yield point |