1.0130 (P265S)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Quality Steel (General Structural Steels with Rm < 500 MPa) |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Al, % |
P, % |
C, % |
S, % |
|---|
| EN 10207 |
97.83–99.5 |
< 0.4 |
0.5–1.5 |
< 0.02 |
< 0.025 |
< 0.2 |
< 0.025 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % |
$$KV_{L}$$, $$J$$ |
Treatment |
|---|
|
|
|
|
normalization |
410–530 |
|
|
|
28 |
|
|
|
< 16 |
|
normalization |
|
265 |
|
|
|
|
|
|
16–40 |
|
normalization |
|
255 |
|
|
|
|
|
|
40–60 |
|
normalization |
|
245 |
|
22 |
|
|
|
|
2–2.5 |
|
normalization |
|
|
17 |
|
|
|
|
|
2.5–3 |
|
normalization |
|
|
18 |
|
|
|
|
|
3–40 |
|
normalization |
|
|
|
22 |
|
|
Properties
| Property |
|---|
| According to EN 10207 Thickness: < 2.5 mm ; yield strength: > 265 MPa |
| According to EN 10207 Thickness: < 2.5 mm ; tensile strength: 410 - 530 MPa |
| According to EN 10207 Thickness: < 2.5 mm ; elongation: > 17 % |
| According to EN 10207 Thickness: < 2.5 mm ; Work strike KV at -20°C [-4°F]: > 28 joules |
| According to EN 10207 Thickness: 2.5 - 3.0 mm ; yield strength: > 265 MPa |
| According to EN 10207 Thickness: 2.5 - 3.0 mm ; tensile strength: 410 - 530 MPa |
| According to EN 10207 Thickness: 2.5 - 3.0 mm ; elongation: > 18 % |
| According to EN 10207 Thickness: 2.5 - 3.0 mm ; Work strike KV at -20°C [-4°F]: > 28 joules |
| According to EN 10207 Thickness: 3 - 16 mm ; yield strength: > 265 MPa |
| According to EN 10207 Thickness: 3 - 16 mm ; yield strength: 410 - 530 MPa |
| According to EN 10207 Thickness: 3 - 16 mm ; elongation: > 22 % |
| According to EN 10207 Thickness: 3 - 16mm ; Work strike KV at -20°C [-4°F]: > 28 joules |
| According to EN 10207 Thickness: 16 - 40 mm ; yield strength: > 255 MPa |
| According to EN 10207 Thickness: 16 - 40 mm ; yield strength: 410 - 530 MPa |
| According to EN 10207 Thickness: 16 - 40 mm ; elongation: > 22 % |
| According to EN 10207 Thickness: 16 - 40 mm ; Work strike KV at -20°C [-4°F]: > 28 joules |
| According to EN 10207 Thickness: 40 - 60 mm ; yield strength: > 245 MPa |
| According to EN 10207 Thickness: 40 - 60mm ; tensile strength: 410 - 530 MPa |
| According to EN 10207 Thickness: 40 - 60 mm ; elongation: > 22 % |
| According to EN 10207 Thickness: 40 - 60mm ; Work strike KV at -20°C [-4°F]: > 28 joules |
| Density: 7.85 g/cm3 |
| Weldability In ISO/TR 20172 Group: 1.1 |
Analogues
| Germany |
CIS, Russia, Ukraine |
USA |
|---|
| BGH 0425 |
16K |
P265GH |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ |
% |
Elongation at break (longitudinal) (for L0 = 5.65√So) |
| $$KV_{L}$$ |
$$J$$ |
Impact energy (longitudinal) |