| According to EN 10025-2 Thickness: < 3 mm ; yield strength: > 275 MPa |
| According to EN 10025-2 Thickness: < 3 mm ; tensile strength: 430 - 580 MPa |
| According to EN 10025-2 Thickness: 3 - 16 mm ; yield strength: > 275 MPa |
| According to EN 10025-2 Thickness: 3 - 16 mm ; yield strength: 410 - 560 MPa |
| According to EN 10025-2 Thickness: 16 - 40 mm ; yield strength: > 265 MPa |
| According to EN 10025-2 Thickness: 16 - 40 mm ; yield strength: 410 - 560 MPa |
| According to EN 10025-2 Thickness: 40 - 63 mm ; yield strength: > 255 MPa |
| According to EN 10025-2 Thickness: 40 - 63 mm ; yield strength: 410 - 560 MPa |
| According to EN 10025-2 Thickness: 63 - 80 mm ; yield strength: > 245 MPa |
| According to EN 10025-2 Thickness: 63 - 80 mm ; tensile strength: 410 - 560 MPa |
| According to EN 10025-2 Thickness: 80 - 100 mm ; yield strength: > 235 MPa |
| According to EN 10025-2 Thickness: 80 - 100 mm ; yield strength: 410 - 560 MPa |
| According to EN 10025-2 Thickness: 100 - 150 mm ; yield strength: > 225 MPa |
| According to EN 10025-2 Thickness: 100 - 150 mm ; yield strength: 400 - 540 MPa |
| According to EN 10025-2 Thickness: 150 - 200 mm ; yield strength: > 215 MPa |
| According to EN 10025-2 Thickness: 150 - 200 mm ; tensile strength: 380 - 540 MPa |
| According to EN 10025-2 Thickness: 200 - 250 mm ; yield strength: > 205 MPa |
| According to EN 10025-2 Thickness: 200 - 250 mm ; tensile strength: 380 - 540 MPa |
| According to EN 10025-2 Thickness: 250 - 400 mm ; yield strength: > 195 MPa |
| According to EN 10025-2 Thickness: 250 - 400 mm ; tensile strength: 380 - 540 MPa |
| According to EN 10025-2 Longitudinal samples Thickness: < 1 mm ; elongation: > 15 % |
| According to EN 10025-2 Longitudinal samples Thickness: 1.0 - 1.5 mm ; elongation: > 16 % |
| According to EN 10025-2 Longitudinal samples Thickness: 1.5 - 2.0 mm ; elongation: > 17 % |
| According to EN 10025-2 Longitudinal samples Thickness: 2.0 - 2.5 mm ; elongation: > 18 % |
| According to EN 10025-2 Longitudinal samples Thickness: 2.5 - 3.0 mm ; elongation: > 19 % |
| According to EN 10025-2 Longitudinal samples Thickness: 3 - 40 mm ; elongation: > 23 % |
| According to EN 10025-2 Longitudinal samples Thickness: 40 - 63 mm ; elongation: > 22 % |
| According to EN 10025-2 Longitudinal samples Thickness: 63 - 100 mm ; elongation: > 21 % |
| According to EN 10025-2 Longitudinal samples Thickness: 100 - 150 mm ; elongation: > 19 % |
| According to EN 10025-2 Longitudinal samples Thickness: 150 - 250 mm ; elongation: > 18 % |
| According to EN 10025-2 Longitudinal sample Thickness: 250 - 400 mm ; elongation: > 18 % |
| According to EN 10025-2 Transverse specimens Thickness: < 1 mm ; elongation: > 13 % |
| According to EN 10025-2 Transverse specimens Thickness: 1.0 - 1.5 mm ; elongation: > 14 % |
| According to EN 10025-2 Transverse specimens Thickness: 1.5 - 2.0 mm ; elongation: > 15 % |
| According to EN 10025-2 Transverse specimens Thickness: 2.0 - 2.5 mm ; elongation: > 16 % |
| According to EN 10025-2 Transverse specimens Thickness: 2.5 - 3.0 mm ; elongation: > 17 % |
| According to EN 10025-2 Transverse specimens Thickness: 3 - 40 mm ; elongation: > 21 % |
| According to EN 10025-2 Transverse specimens Thickness: 40 - 63 mm ; elongation: > 20 % |
| According to EN 10025-2 Transverse specimens Thickness: 63 - 100 mm ; elongation: > 19 % |
| According to EN 10025-2 Transverse specimens Thickness: 100 - 150 mm ; elongation: > 19 % |
| According to EN 10025-2 Transverse specimens Thickness: 150 - 250 mm ; elongation: > 18 % |
| According to EN 10025-2 Transverse specimens Thickness: 250 - 400 mm ; elongation: > 18 % |
| According to EN 10025-2 Test for impact strength Thickness: < 150 mm ; Work strike KV at -20°C [-4°F]: > 27 j |
| According to EN 10025-2 Test for impact strength Thickness: 150 - 250 mm ; Work strike KV at -20°C [-4°F]: > 27 j |
| According to EN 10025-2 Test for impact strength Thickness: 250 - 400 mm ; Work strike KV at -20°C [-4°F]: > 27 j |
| According to EN 10025-2 bend Test of the note is Used for bending angle < 90° |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 1.0 - 1.5 mm ; bending Radius: > 2 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 1.5 - 2.5 mm ; bending Radius: > 3 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 2.5 - 3.0 mm ; bending Radius: > 4 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 3 - 4 mm ; bending Radius: > 6 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 4 - 5 mm ; bending Radius: > 10 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 5 - 6mm ; bending Radius: > 12 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 6 - 7 mm ; bending Radius: > 16 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 7 - 8 mm ; bending Radius: > 20 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 8 - 10mm ; bending Radius: > 25 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal sample Thickness: 10 - 12mm ; bending Radius: > 32 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 12 - 14 mm ; bending Radius: > 36mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 14 - 16 mm ; bending Radius: > 40 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 16 - 18 mm ; bending Radius: > 45 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal samples Thickness: 18 - 20mm ; bending Radius: > 50 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal sample Thickness: 20 - 25mm ; bending Radius: > 60 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging the Longitudinal sample Thickness: 25 - 30 mm ; bending Radius: > 75 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 1.0 - 1.5 mm ; bending Radius: > 2 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 1.5 - 2.5 mm ; bending Radius: > 3 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 2.5 - 3.0 mm ; bending Radius: > 4 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 3 - 4 mm ; bending Radius: > 5 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 4 - 5 mm ; bending Radius: > 8 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 5 - 6mm ; bending Radius: > 10 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 6 - 7 mm ; bending Radius: > 12 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 7 - 8 mm ; bending Radius: > 16 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 8 - 10mm ; bending Radius: > 20 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 10 - 12mm ; bending Radius: > 25 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 12 - 14 mm ; bending Radius: > 28 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 14 - 16 mm ; bending Radius: > 32 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 16 - 18 mm ; bending Radius: > 40 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 18 - 20mm ; bending Radius: > 45 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 20 - 25mm ; bending Radius: > 55 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold flanging Transverse specimens Thickness: 25 - 30 mm ; bending Radius: > 70 mm |
| According to EN 10025-2 bend Test of hot rolled plates, cold profiling Thickness: < 6 mm ; the bend Test in cold state: r > t |
| According to EN 10025-2 bend Test of hot rolled plates, cold profiling Thickness: 6 - 8mm ; Test cold bending: r > 1.5 t |
| Density: 7.85 g / cm3 |
| Weldability ISO 15608 Group 1.1 |