1.0213 (C8C)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Other Structural Steels (Not Intended for Heat Treatment with Rm < 500 MPa) |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Al, % |
P, % |
C, % |
S, % |
|---|
| EN 10263-2 |
99.245–99.67 |
< 0.1 |
0.25–0.45 |
0.02–0.06 |
< 0.02 |
0.06–0.1 |
< 0.025 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\psi$$, % |
Treatment |
|---|
|
|
|
|
|
340–490 |
65–72 |
|
Properties
| Property |
|---|
| According to EN 10263-2 +U or +U+PE tensile strength: < 410 MPa |
| According to EN 10263-2 +U or +U+PE Relative contraction: > 65 % |
| According to EN 10263-2 +or AC +AC+PE tensile strength: < 360 MPa |
| According to EN 10263-2 +or AC +AC+PE Relative contraction: > 70 % |
| According to EN 10263-2 +U+C Diameter: 5 - 10mm ; tensile strength: < 490 MPa |
| According to EN 10263-2 +U+C Diameter: 5 - 10mm ; Relative narrowing: > 63 % |
| According to EN 10263-2 +U+C Diameter: 10 - 40 mm ; yield strength: < 480 MPa |
| According to EN 10263-2 +U+C Diameter: 10 - 40 mm ; the Relative narrowing: > 63 % |
| According to EN 10263-2 +U+C+AC Diameter: 2 - 5mm ; tensile strength: < 350 MPa |
| According to EN 10263-2 +U+C+AC Diameter: 2 - 5mm ; the Relative narrowing: > 72 % |
| According to EN 10263-2 +U+C+AC Diameter: 5 - 40 mm ; yield strength: < 340 MPa |
| According to EN 10263-2 +U+C+AC Diameter: 5 - 40 mm ; the Relative narrowing: > 72 % |
| According to EN 10263-2 +U+C+AC+LC Diameter: 2 - 5mm ; tensile strength: < 390 MPa |
| According to EN 10263-2 +U+C+AC+LC Diameter: 2 - 5mm ; the Relative narrowing: > 68 % |
| According to EN 10263-2 +U+C+AC+LC Diameter: 5 - 40 mm ; yield strength: < 380 MPa |
| According to EN 10263-2 +U+C+AC+LC Diameter: 5 - 40 mm ; the Relative narrowing: > 68 % |
| According to EN 10263-2 +AC+C Diameter: 5 - 10mm ; tensile strength: < 450MPa |
| According to EN 10263-2 +AC+C Diameter: 5 - 10mm ; Relative narrowing: > 65 % |
| According to EN 10263-2 +AC+C Diameter: 10 - 40 mm ; yield strength: < 440 MPa |
| According to EN 10263-2 +AC+C Diameter: 10 - 40 mm ; the Relative narrowing: > 65 % |
| Density: 7.86 g / cm3 |
Analogues
| Germany |
CIS, Russia, Ukraine |
USA |
|---|
| D 8-2 |
08U |
SAE 1008 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\psi$$ |
% |
Reduction in cross section on fracture |