1.0236 (E315)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Other Structural Steels (Not Intended for Heat Treatment with Rm < 500 MPa) |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
P, % |
C, % |
S, % |
|---|
| DIN EN 10297-1:2003 |
> 97.925 |
< 0.3 |
< 1.5 |
< 0.03 |
< 0.21 |
< 0.035 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\epsilon_T$$, % |
Treatment |
|---|
|
|
< 16 |
|
rolling |
450 |
315 |
21 |
19 |
|
|
|
16–40 |
|
rolling |
450 |
305 |
|
|
|
|
|
40–65 |
|
rolling |
450 |
295 |
|
|
|
|
|
65–100 |
|
rolling |
420 |
|
|
|
|
|
|
65–80 |
|
rolling |
|
280 |
|
|
|
|
|
80–100 |
|
rolling |
|
270 |
|
|
|
Properties
| Property |
|---|
| According to EN 10297-1 note the Normalization 890 - 950°C |
| According to EN 10297-1 +AR or +N wall Thickness: < 16 mm ; yield strength: > 315 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: < 16 mm ; yield strength: > 450 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 16 - 40 mm ; yield strength: > 305 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 16 - 40 mm ; yield strength: > 450 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 40 - 65 mm ; yield strength: > 295 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 40 - 65 mm ; tensile strength: > 450 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 65 - 80 mm ; yield strength: > 280 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 65 - 80 mm ; yield strength: > 420 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 80 - 100 mm ; yield strength: > 270 MPa |
| According to EN 10297-1 +AR or +N wall Thickness: 80 - 100 mm ; yield strength: > 420 MPa |
| According to EN 10297-1 +AR or +N Longitudinal specimens elongation: > 21 % |
| According to EN 10297-1 +AR or +N Transverse specimens elongation: > 19 % |
| Weldability In ISO/TR 20172 Group: 1.2 |
| Density: 7.84 g / cm3 |
Analogues
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\epsilon_T$$ |
% |
Elongation at break (transverse) |