1.0305 (P235G1TH)
Classification
| Country | Section | Category |
|---|---|---|
| Germany | Non-alloy Steels | Steels with Average C < 0,12% or Rm < 400 MPa |
Chemical composition
| Standard | Fe, % | Si, % | Mn, % | P, % | C, % | S, % |
|---|---|---|---|---|---|---|
| EN 50112 | 98.6–99.5 | 0.1–0.35 | 0.4–0.8 | < 0.04 | < 0.17 | < 0.04 |
Information on suppliers
Properties
| Property |
|---|
| According to DIN 17175 Thickness: < 16 mm ; yield strength: > 235 MPa |
| According to DIN 17175 Thickness: < 16 mm ; yield strength: 360 - 480 MPa |
| According to DIN 17175 Thickness: 16 - 40 mm ; yield strength: > 225 MPa |
| According to DIN 17175 Thickness: 16 - 40 mm ; yield strength: 360 - 480 MPa |
| According to DIN 17175 Thickness: > 40 mm ; yield strength: > 215 MPa |
| According to DIN 17175 Thickness: > 40 mm ; yield strength: 360 - 480 MPa |
| According to DIN 17175 Longitudinal specimens elongation: > 25 % |
| According to DIN 17175 Transverse specimens elongation: > 23 % |
| According to DIN 17175 Transverse samples Job blow KV at 20°C [68°F]: > 34 j |
| Density: 7.85 g / cm3 |
Analogues
| Germany | CIS, Russia, Ukraine | USA |
|---|---|---|
| DIRO-H I | 10PP | P235GH |
Standards
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| Mn | % | Manganese |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |