1.0332 (DD11)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Steels with Average C < 0,12% or Rm < 400 MPa |
Chemical composition
| Standard |
Fe, % |
Mn, % |
P, % |
C, % |
S, % |
|---|
| EN 10111 |
> 99.19 |
< 0.6 |
< 0.045 |
< 0.12 |
< 0.045 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_{L (L_0 = 80 mm)}$$, % |
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % |
Treatment |
|---|
|
|
|
|
|
440 |
|
|
|
|
|
|
1–2 |
|
|
|
170–360 |
|
|
|
|
|
2–11 |
|
|
|
170–340 |
|
|
|
|
|
1–1.5 |
|
|
|
|
22 |
|
|
|
|
1.5–2 |
|
|
|
|
23 |
|
|
|
|
2–3 |
|
|
|
|
24 |
|
|
|
|
3–11 |
|
|
|
|
|
28 |
|
Properties
| Property |
|---|
| According to EN 10111 Thickness: 1.0 - 1.5 mm ; yield strength: 170 - 360 MPa |
| According to EN 10111 Thickness: 1.0 - 1.5 mm ; tensile strength: < 440 MPa |
| According to EN 10111 Thickness: 1.0 - 1.5 mm ; elongation: > 22 % |
| According to EN 10111 Thickness: 1.5 - 2.0 mm ; yield strength: 170 - 360 MPa |
| According to EN 10111 Thickness: 1.5 - 2.0 mm ; tensile strength: < 440 MPa |
| According to EN 10111 Thickness: 1.5 - 2.0 mm ; elongation: > 23 % |
| According to EN 10111 Thickness: 2 - 3 mm ; yield strength: 170 - 340 MPa |
| According to EN 10111 Thickness: 2 - 3mm ; tensile strength: < 440 MPa |
| According to EN 10111 Thickness: 2 - 3 mm ; elongation: > 24 % |
| According to EN 10111 Thickness: 3 - 11 mm ; yield strength: 170 - 340 MPa |
| According to EN 10111 Thickness: 3 - 11 mm ; tensile strength: < 440 MPa |
| According to EN 10111 Thickness: 3 - 11 mm ; elongation: > 28 % |
| Density: 7.86 g / cm3 |
Analogues
| Germany |
CIS, Russia, Ukraine |
USA |
|---|
| St 1203 |
15kp |
SAE 1008 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Mn |
% |
Manganese |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_{L (L_0 = 80 mm)}$$ |
% |
Elongation at break (longitudinal) (for L0 = 80 mm) |
| $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ |
% |
Elongation at break (longitudinal) (for L0 = 5.65√So) |