1.0342
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Steels with Average C < 0,12% or Rm < 400 MPa |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Al, % |
P, % |
C, % |
S, % |
|---|
| DIN EN 10268:2006 |
98.83–99.985 |
< 0.4 |
< 0.6 |
> 0.015 |
< 0.08 |
< 0.05 |
< 0.025 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{0.2}$$, $$MPa$$ |
$$\epsilon_{L (L_0 = 80 mm)}$$, % |
Treatment |
|---|
|
|
|
|
|
280–360 |
180–230 |
34 |
|
Properties
| Property |
|---|
| According to EN 10268 Transverse specimens Thickness: < 0.5 mm ; yield strength: 180 - 230 MPa |
| According to EN 10268 Transverse specimens Thickness: < 0.5 mm ; tensile strength: 280 - 360 MPa |
| According to EN 10268 Transverse specimens Thickness: < 0.5 mm ; elongation: > 34 % |
| According to EN 10268 Transverse specimens Thickness: 0.5 - 0.7 mm ; yield strength: 180 - 230 MPa |
| According to EN 10268 Transverse specimens Thickness: 0.5 - 0.7 mm ; tensile strength: 280 - 360 MPa |
| According to EN 10268 Transverse specimens Thickness: 0.5 - 0.7 mm ; elongation: > 32 % |
| According to EN 10268 Transverse specimens Thickness: 0.5 - 0.7 mm ; plastic deformation Coefficient (r): > 1.6 |
| According to EN 10268 Transverse specimens Thickness: 0.5 - 0.7 mm ; the Coefficient of strain hardening (n): > 0.17 |
| According to EN 10268 Transverse specimens Thickness: 0.7 - 2.0 mm ; yield strength: 180 - 230 MPa |
| According to EN 10268 Transverse specimens Thickness: 0.7 - 2.0 mm ; tensile strength: 280 - 360 MPa |
| According to EN 10268 Transverse specimens Thickness: 0.7 - 2.0 mm ; elongation: > 34 % |
| According to EN 10268 Transverse specimens Thickness: 0.7 - 2.0 mm ; plastic deformation Coefficient (r): > 1.6 |
| According to EN 10268 Transverse specimens Thickness: 0.7 - 2.0 mm ; the Coefficient of strain hardening (n): > 0.17 |
| According to EN 10268 Transverse specimens Thickness: > 2 mm ; yield strength: 180 - 230 MPa |
| According to EN 10268 Transverse specimens Thickness: > 2 mm ; tensile strength: 280 - 360 MPa |
| According to EN 10268 Transverse specimens Thickness: > 2 mm ; elongation: > 34 % |
| According to EN 10268 Transverse specimens Thickness: > 2 mm ; plastic deformation Coefficient (r): > 1.4 |
| According to EN 10268 Transverse specimens Thickness: > 2 mm ; the Coefficient of strain hardening (n): > 0.17 |
| Weldability In ISO/TR 20172 Group: 1.1 |
| Density: 7.85 g/cm3 |
Analogues
| Germany |
CIS, Russia, Ukraine |
|---|
| HC180P |
HC180P |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{0.2}$$ |
$$MPa$$ |
Tensile stress required to produce a total elongation of 0.2% |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_{L (L_0 = 80 mm)}$$ |
% |
Elongation at break (longitudinal) (for L0 = 80 mm) |