σU
MPa
σY
MPa
ϵL(L0=5.65So√)
KVL
J
KVT
J

1.0491 (S275NL)

Durable at low temperatures

Classification

Country	Section	Category
Country	Section	Category
Germany	Non-alloy Steels	Steels with Average 0,12% =< C < 0,25% or 400 MPa = < Rm < 500 MPa

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Cu, %	Ni, %	V, %	Al, %	P, %	C, %	S, %	Nb, %	Mo, %	N, %	CEV, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Cu, %	Ni, %	V, %	Al, %	P, %	C, %	S, %	Nb, %	Mo, %	N, %	CEV, %
	96.04–99.5	< 0.4	0.5–1.5	< 0.3	< 0.05	< 0.55	< 0.3	< 0.05	< 0.02	< 0.025	< 0.16	< 0.02	< 0.05	< 0.1	< 0.015	< 0.42

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
		< 100			370–510
		100–200			350–480
		200–250			350–480	205	23
		< 16				275	24
		16–40				265	24
		40–63				255	24
		63–80				245	23
		80–100				235
		100–150				225
		150–200				215
				normalization				63	40
		80–200					23

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ti	%	Titan
Cu	%	Copper
Ni	%	Nickel
V	%	Vanadium
Al	%	Aluminium
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Nb	%	Niobium
Mo	%	Molybdenum
N	%	Nitrogen
CEV	%	Cerium

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$	%	Elongation at break (longitudinal) (for L₀ = 5.65√So)
$KV_{L}$	$J$	Impact energy (longitudinal)
$KV_{T}$	$J$	Impact energy (transverse)