1.0509 (E410)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Steels with Average 0,25% =< C < 0,55% or 500 MPa =< Rm < 700 MPa |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Ti, % |
V, % |
Al, % |
P, % |
C, % |
S, % |
Nb, % |
|---|
| EN 10305-1 |
97.185–98.35 |
0.1–0.5 |
1.3–1.7 |
< 0.05 |
0.08–0.15 |
0.01–0.06 |
< 0.03 |
0.16–0.22 |
< 0.035 |
< 0.07 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
|
|
|
|
solid, cold drawn |
750 |
|
4 |
|
|
|
|
|
soft, cold drawn |
620 |
|
8 |
|
|
|
|
|
annealing, soft |
520 |
|
22 |
|
|
|
|
|
cold drawn, stress relief |
690 |
590 |
12 |
|
|
|
|
|
normalization |
550–700 |
410 |
|
|
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Ti |
% |
Titan |
| V |
% |
Vanadium |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Nb |
% |
Niobium |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |