1.1141 (C15E)

Classification

Country Section Category
Germany Non-alloy Special Steels Structural Pressure Vessel and Engineering Steels with C < 0,5%

Chemical composition

Standard Fe, % Si, % Mn, % P, % C, % S, %
EN 10084 98.75–99.58 < 0.4 0.3–0.6 < 0.035 0.12–0.18 < 0.035

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_{L (L_0 = 80 mm)}$$, % Treatment
annealing, soft 450 360 25
cold rolling 870

Brinell hardness number

Rolling Standard Classifiers Value, HBW
annealing, soft 143
normalization 95–150

Твёрдость по Роквеллу

Rolling Standard Classifiers Value, HRC
annealing, soft 76

Твёрдость по Викерсу

Rolling Standard Classifiers Value, HV
annealing, soft 140
cold rolling 260

Technological Properties

Weldability
no limits

Standards

Standard Description
EN 10084

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
P % Phosphorus
C % Carbon
S % Sulfur

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_{L (L_0 = 80 mm)}$$ % Elongation at break (longitudinal) (for L0 = 80 mm)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures