1.1179 (C30R)

Classification

Country	Section	Category
Country	Section	Category
Germany	Non-alloy Special Steels	Structural Pressure Vessel and Engineering Steels with C < 0,5%

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %
EN 10083-1	97.485–99.21	< 0.4	0.5–0.8	< 0.4	< 0.4	< 0.035	0.27–0.34	0.02–0.04	< 0.1

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KU$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KU$ , $J$	Treatment
		< 16			600–750	> 400	< 18	< 40	< 40	After hardening and tempering
		17–40			550–700	> 350	< 20	< 45	< 40	After hardening and tempering
		41–100			500–650	> 300	< 21	< 50	< 40	After hardening and tempering

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
		soft, annealing	< 170

Standards

Standard	Description
Standard	Description
EN 10083-1

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KU$	$J$	Impact energy