1.1181 (C35E)

Classification

Country Section Category
Germany Non-alloy Special Steels Structural Pressure Vessel and Engineering Steels with C < 0,5%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, % Mo, %
EN 10083-1 97.445–99.18 < 0.4 0.5–0.8 < 0.4 < 0.4 < 0.03 0.32–0.39 < 0.035 < 0.1

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % $$\epsilon_T$$, % $$R_{eH}$$, $$MPa$$ $$KV_{L}$$, $$J$$ $$KV_{T}$$, $$J$$ Treatment
< 16 normalization 550 21 18 15 300 27
16–100 normalization 520 19 270
100–250 normalization 500 19 245
250–500 normalization 480 220
500–1000 normalization 470 210
0.3–3 annealing, soft 540 430 22
0.3–3 cold rolling 930
5–10 solid, cold drawn 650–1000 510 6
10–16 solid, cold drawn 600–950 420 7
16–40 solid, cold drawn 580–880 320 8
40–63 solid, cold drawn 550–840 300 9
63–100 solid, cold drawn 520–800 270 9
< 8 moderate hardening 630 430 17 35 22
8–20 moderate hardening 600 380 19
20–50 moderate hardening 550 320 20
50–80 moderate hardening 500 290 20
< 100 normalization 270

Brinell hardness number

Rolling Standard Classifiers Value, HBW
rolling, turning 154–207
annealing, soft 183

Твёрдость по Викерсу

Rolling Standard Classifiers Value, HV
cold rolling 275
annealing, soft 170

Technological Properties

Weldability
no limits

Standards

Standard Description
EN 10083-1

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ % Elongation at break (longitudinal) (for L0 = 5.65√So)
$$\epsilon_T$$ % Elongation at break (transverse)
$$R_{eH}$$ $$MPa$$ Upper yield point
$$KV_{L}$$ $$J$$ Impact energy (longitudinal)
$$KV_{T}$$ $$J$$ Impact energy (transverse)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures