1.1186 (C40E)

Classification

Country Section Category
Germany Non-alloy Special Steels Structural Pressure Vessel and Engineering Steels with C < 0,5%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, % Mo, %
97.395–99.13 < 0.4 0.5–0.8 < 0.4 < 0.4 < 0.03 0.37–0.44 < 0.035 < 0.1

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % $$\epsilon_{L (L_0 = 80 mm)}$$, % $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % $$R_{eH}$$, $$MPa$$ $$KV_{L}$$, $$J$$ Treatment
< 16 normalization 580 16 320
16–100 normalization 550 17 290
100–250 normalization 530 17 260
0.3–3 annealing, soft 550 440 18
0.3–3 cold rolling 970
5–10 solid, cold drawn 700–1000 540 6
10–16 solid, cold drawn 650–980 460 7
16–40 solid, cold drawn 620–920 365 8
40–63 solid, cold drawn 590–840 330 9
63–100 solid, cold drawn 550–820 290 9
moderate hardening 30

Brinell hardness number

Rolling Standard Classifiers Value, HBW
rolling, turning 163–211

Твёрдость по Викерсу

Rolling Standard Classifiers Value, HV
cold rolling 280
annealing, soft 170

Technological Properties

Weldability
Boundedly welded

Analogues

CIS, Russia, Ukraine
40

Standards

Standard Description
EN 10083-1
EN 10132-3

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\epsilon_{L (L_0 = 80 mm)}$$ % Elongation at break (longitudinal) (for L0 = 80 mm)
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ % Elongation at break (longitudinal) (for L0 = 5.65√So)
$$R_{eH}$$ $$MPa$$ Upper yield point
$$KV_{L}$$ $$J$$ Impact energy (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures