1.1203 (C55E)

Classification

Country Section Category
Germany Non-alloy Special Steels Structural Pressure Vessel and Engineering Steels with C > = 0,5%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, % Mo, %
EN 10083-1 97.135–98.88 < 0.4 0.6–0.9 < 0.4 < 0.4 < 0.03 0.52–0.6 < 0.035 < 0.1

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_{L (L_0 = 80 mm)}$$, % $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % $$R_{eH}$$, $$MPa$$ Treatment
< 16 normalization 680 11 370
16–100 normalization 640 12 330
100–250 normalization 620 12 300
250–500 normalization 600 260
500–1000 normalization 590 250
0.3–3 annealing, soft 600 480 17
0.3–3 moderate hardening 1100–1700

Brinell hardness number

Rolling Standard Classifiers Value, HBW
improved machinability 255
annealing, soft 229

Твёрдость по Викерсу

Rolling Standard Classifiers Value, HV
annealing, soft 185
cold rolling 300
moderate hardening 340–520

Standards

Standard Description
EN 10083-1

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_{L (L_0 = 80 mm)}$$ % Elongation at break (longitudinal) (for L0 = 80 mm)
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ % Elongation at break (longitudinal) (for L0 = 5.65√So)
$$R_{eH}$$ $$MPa$$ Upper yield point