1.1206 (C50E)

Classification

Country Section Category
Germany Non-alloy Special Steels Structural Pressure Vessel and Engineering Steels with C > = 0,5%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, % Mo, %
EN 10083-1 97.185–98.93 < 0.4 0.6–0.9 < 0.4 < 0.4 < 0.03 0.47–0.55 < 0.035 < 0.1

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % $$\epsilon_{L (L_0 = 80 mm)}$$, % $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % $$R_{eH}$$, $$MPa$$ Treatment
< 16 normalization 650 13 355
16–100 normalization 610 14 320
100–250 normalization 590 14 290
0.3–3 annealing, soft 580 465 17
0.3–3 cold rolling 1050
0.3–3 moderate hardening 1050–1650
5–10 solid, cold drawn 770–1100 590 5
10–16 solid, cold drawn 730–1080 520 6
16–40 solid, cold drawn 690–1050 440 7
40–63 solid, cold drawn 650–1030 390 8

Brinell hardness number

Rolling Standard Classifiers Value, HBW
improved machinability 255
annealing, soft 217
rolling, turning 181–269

Твёрдость по Викерсу

Rolling Standard Classifiers Value, HV
cold rolling 295
annealing, soft 180
moderate hardening 325–505

Technological Properties

Weldability
Not applicable for welded structures

Standards

Standard Description
EN 10083-1

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\epsilon_{L (L_0 = 80 mm)}$$ % Elongation at break (longitudinal) (for L0 = 80 mm)
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ % Elongation at break (longitudinal) (for L0 = 5.65√So)
$$R_{eH}$$ $$MPa$$ Upper yield point

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures