1.3962 (X15CrNiMn12-10)

Classification

Country	Section	Category
Country	Section	Category
Germany	Alloy Miscellaneous Steels	Materials with Special Physical Properties and with Ni

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	N, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	N, %
SEW390	69.025–74.95	< 0.6	5.5–6.5	10.5–12.5	9–11	< 0.045	0.05–0.2	< 0.03	< 0.1

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	195		7900	0.7
100		16.5
200		17.5
300		18.5
400		19.5

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$KU$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$KU$ , $J$	Treatment
					500–700	< 215	< 45	> 137	hardening
					640–880	< 390	< 40	> 124	Hot-cold treatment
					640–830	< 490	< 35	< 103	Cold processing

Standards

Standard	Description
Standard	Description
SEW390

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$KU$	$J$	Impact energy