1.4027 (GX20Cr14)

Classification

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Stainless Steel with Ni < 2.5% without Mo, Nb and Ti

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %
SEW410	82.195–87.34	< 1	< 1	12.5–14.5	< 1	< 0.045	0.16–0.23	< 0.03

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$
Temperature, °C	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$
20		29	7700	0.46
100	10.5
200	11
300	11.5
400	11.5
500	12

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	Treatment
					590–790	< 440	< 12	Hot Processing

Analogues

CIS, Russia, Ukraine
CIS, Russia, Ukraine
20H13L

Standards

Standard	Description
Standard	Description
SEW410

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$c\cdot 10^{-3}$	$\frac{J}{kg\cdot K}$	The specific heat of the material (range 20°C–T)

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)