1.4362 (X2CrNiN23-4)

Classification

Country Section Category
Germany Stainless and Heat Resisting Steels Stainless Steel with Ni ≥ 2.5% without Mo, Nb and Ti

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % P, % C, % S, % Mo, % N, %
66.02–74.25 < 1 < 2 22–24 0.1–0.6 3.5–5.5 < 0.035 < 0.03 < 0.015 0.1–0.6 0.05–0.2

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 200 15 7800 0.5 0.8
100 13
200 13.5
300 14

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % $$\epsilon_T$$, % $$KV_{L}$$, $$J$$ $$KV_{T}$$, $$J$$ Treatment
annealing, soft 600–850 400–450 20–25 100–120 90
solution annealing 600–820 400 25 25 120

Brinell hardness number

Rolling Standard Classifiers Value, HBW
annealing, soft 260
solution annealing 290

Analogues

CIS, Russia, Ukraine
ZI68

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum
N % Nitrogen

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\epsilon_T$$ % Elongation at break (transverse)
$$KV_{L}$$ $$J$$ Impact energy (longitudinal)
$$KV_{T}$$ $$J$$ Impact energy (transverse)