1.4415 (X2CrNiMoV13-5-2)

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Stainless Steel with Ni > = 2.5% with Mo but without Nb and Ti

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	V, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	V, %	P, %	C, %	S, %	Mo, %
	75.905–82.4	< 0.5	< 0.5	11.5–13.5	< 0.01	4.5–6.5	0.1–0.5	< 0.04	< 0.03	< 0.015	1.5–2.5

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$KV_{L}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$KV_{L}$ , $J$	Treatment
				moderate hardening	750–1000	650–750	15–18	80–100

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$KV_{L}$	$J$	Impact energy (longitudinal)