1.4432 (X2CrNiMo17-12-3)

Classification

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Stainless Steel with Ni > = 2.5% with Mo but without Nb and Ti

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %	N, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %	N, %
	62.3–70.5	< 1	< 2	16.5–18.5	10.5–13	< 0.045	< 0.03	< 0.015	2.5–3	< 0.11

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
				annealing, soft	490–700	190–240	40–45		100	60
				solution annealing	490–690	190	40
				solid, solution annealing, cold drawn	750–780
		2–50						63–68

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
		annealing, soft	215
		solution annealing	200

Standards

Standard	Description
Standard	Description
EN 10028-7
EN 10038-1

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum
N	%	Nitrogen

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KV_{L}$	$J$	Impact energy (longitudinal)
$KV_{T}$	$J$	Impact energy (transverse)