1.4532 (X8CrNiMoAl15-7-2)

Classification

Country Section Category
Germany Stainless and Heat Resisting Steels Stainless Steels with Special Additions

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % Al, % P, % C, % S, % Mo, %
69.645–76.8 < 0.7 < 1.2 14–16 6.5–7.8 0.7–1.5 < 0.04 < 0.1 < 0.015 2–3

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 200 16 7800 0.5 0.8
100 14
300 14.4

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
< 6 < 1100 < 20 Annealing. Cold rolled strip.
< 6 < 1550 < 1380 < 20 Hardening. Cold rolled strip.

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
Al % Aluminium
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)