1.4585 (GX7CrNiMoCuNb18-18)

Classification

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Stainless Steels with Special Additions

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %	Mo, %
	51.945–60.7	< 1.5	< 2	16.5–18.5	1.8–2.4	19–21	< 0.045	< 0.08	< 0.03	2–2.5

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$
Temperature, °C	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$
20		15	7900	0.5
100	16.5
200	17
300	17.5
400	18
500	18.5

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	Treatment
					440–640	< 175	< 15	hardening

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$c\cdot 10^{-3}$	$\frac{J}{kg\cdot K}$	The specific heat of the material (range 20°C–T)

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)