α⋅106
K−1
ϰ
Wm⋅K
ρ
kgm3
σU
MPa
σ0.2
MPa
ϵL
ψ

1.4704 (45SiCr16-11)

Classification

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Heat Resistant Steels with Ni < 2.5%

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	P, %	C, %	S, %
	90.925–93.6	3.5–4.5	< 1	2.5–3	< 0.045	0.4–0.5	< 0.03

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$
Temperature, °C	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$
20		17	7750
500	12.3
700	12.5

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	Treatment
					880–1030	< 685	< 14	< 40	After treatment and aging

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture