1.4875 (X55CrMnNiN20-8)

Classification

Country Section Category
Germany Stainless and Heat Resisting Steels Heat Resistant Steels with Ni > = 2.5%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, % N, %
EN 10090 64.425–71.3 < 0.25 7–10 19.5–21.5 1.5–2.75 < 0.045 0.5–0.6 < 0.03 0.2–0.4

Information on suppliers

Physical characteristics

Temperature, °C $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$
20 14.5 7800
100 15.5
300 17.5
500 18.5
700 18.8

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % $$\psi$$, % Treatment
solution annealing 900–1150 550 8 10

Твёрдость по Роквеллу

Rolling Standard Classifiers Value, HRC
solution annealing 28

Standards

Standard Description
EN 10090

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
N % Nitrogen

Description of physical characteristics

Parameter Units of measurement Description
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\psi$$ % Reduction in cross section on fracture