1.4876 (X10NiCrAlTi32-20)

Filler material 2.4806

Classification

Country Section Category
Germany Stainless and Heat Resisting Steels Heat Resistant Steels with Ni > = 2.5%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ti, % Ni, % Al, % P, % C, % S, %
38.635–50.7 < 1 < 2 19–23 0.15–0.6 30–34 0.15–0.6 < 0.03 < 0.12 < 0.015

Information on suppliers

Physical characteristics

Temperature, °C $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 12 8000 0.55 1
400 16
800 17.5
1000 18.5

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{0.2}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
solution annealing 450–680 170 28–30

Brinell hardness number

Rolling Standard Classifiers Value, HBW
solution annealing 192

Analogues

USA CIS, Russia, Ukraine
N08800 X8NiCrAlTi32-21

Standards

Standard Description
DIN EN 10088-1:2014
DIN EN 10095:1999
DIN EN 10297-2:2005
SEW470

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ti % Titan
Ni % Nickel
Al % Aluminium
P % Phosphorus
C % Carbon
S % Sulfur

Description of physical characteristics

Parameter Units of measurement Description
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{0.2}$$ $$MPa$$ Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)