1.4877
Classification
| Country |
Section |
Category |
| Germany |
Stainless and Heat Resisting Steels |
Heat Resistant Steels with Ni > = 2.5% |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
Al, % |
Ce, % |
P, % |
C, % |
S, % |
Nb, % |
N, % |
|---|
|
36.355–42.31 |
< 0.3 |
< 1 |
26–28 |
31–33 |
< 0.025 |
0.05–0.1 |
< 0.02 |
0.04–0.08 |
< 0.01 |
0.6–1 |
< 0.11 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{0.2}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
|
|
|
|
solution annealing |
500–750 |
180 |
35 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
|
|
solution annealing |
223 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| Al |
% |
Aluminium |
| Ce |
% |
Cerium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Nb |
% |
Niobium |
| N |
% |
Nitrogen |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{0.2}$$ |
$$MPa$$ |
Tensile stress required to produce a total elongation of 0.2% |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |