1.4901

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Materials with Elevated Temperature Properties

Standard	Fe, %	Si, %	B, %	Mn, %	Cr, %	Ti, %	Ni, %	V, %	Zr, %	Al, %	P, %	C, %	S, %	Nb, %	Mo, %	N, %	W, %
Standard	Fe, %	Si, %	B, %	Mn, %	Cr, %	Ti, %	Ni, %	V, %	Zr, %	Al, %	P, %	C, %	S, %	Nb, %	Mo, %	N, %	W, %
	85.784–89.109	< 0.5	0.001–0.006	0.3–0.6	8.5–9.5	< 0.01	< 0.4	0.15–0.25	< 0.01	< 0.02	< 0.02	0.07–0.13	< 0.01	0.04–0.09	0.3–0.6	0.03–0.07	1.5–2

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\epsilon_T$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\epsilon_T$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
				Hardening, normalization	620–850	440	19	17	40	27

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\epsilon_T$	%	Elongation at break (transverse)
$KV_{L}$	$J$	Impact energy (longitudinal)
$KV_{T}$	$J$	Impact energy (transverse)