1.5025 (51Si7)
Classification
| Country |
Section |
Category |
| Germany |
Structural, Pressure Vessel and Engineering Steels |
Mn-Si-Cu |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
P, % |
C, % |
S, % |
N, % |
|---|
|
96.753–97.53 |
1.5–1.8 |
0.5–0.8 |
< 0.045 |
0.47–0.55 |
< 0.045 |
< 0.007 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
$$KU$$, $$J$$ |
Treatment |
|---|
|
|
|
|
|
1350–1600 |
> 1150 |
< 6 |
< 25 |
> 14 |
Hardening 840-870 in water. Vacation 430-500 in the air |
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
|
|
soft, annealing |
< 245 |
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| N |
% |
Nitrogen |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
| $$KU$$ |
$$J$$ |
Impact energy |