1.5223 (42MnV7)

Classification

Country	Section	Category
Country	Section	Category
Germany	Structural, Pressure Vessel and Engineering Steels	Mn-Cu, Mn-V, Si-V, Mn-Si-V

Chemical composition

Standard	Fe, %	Si, %	Mn, %	V, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	V, %	P, %	C, %	S, %
	97.11–97.8	0.15–0.35	1.6–1.9	0.07–0.12	< 0.035	0.38–0.45	< 0.035

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KU$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KU$ , $J$	Treatment
		< 16			980–1270	> 885	< 10	< 30	< 15	After hardening and tempering
		17–40			980–1180	> 785	< 11	< 35	< 20	After hardening and tempering
		41–100			880–1030	> 685	< 12	< 40	< 40	After hardening and tempering

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
		soft, annealing	< 217

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
V	%	Vanadium
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KU$	$J$	Impact energy