1.5511 (35B2)
Classification
| Country |
Section |
Category |
| Germany |
Structural, Pressure Vessel and Engineering Steels |
B, Mn-B Mn < 1.65% |
Chemical composition
| Standard |
Fe, % |
Si, % |
B, % |
Mn, % |
Al, % |
P, % |
C, % |
S, % |
|---|
| EN 10269 |
98.315–99.1792 |
< 0.4 |
0.0008–0.005 |
0.5–0.8 |
< 0.02 |
< 0.035 |
0.32–0.39 |
< 0.035 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{0.2}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
$$KV_{L}$$, $$J$$ |
Treatment |
|---|
|
|
|
|
annealing, carbide spheroidization |
570 |
|
|
62 |
|
|
|
|
|
|
moderate hardening |
500–650 |
300 |
22 |
45 |
39–55 |
|
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| B |
% |
Bor |
| Mn |
% |
Manganese |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{0.2}$$ |
$$MPa$$ |
Tensile stress required to produce a total elongation of 0.2% |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
| $$KV_{L}$$ |
$$J$$ |
Impact energy (longitudinal) |