1.5732 (14NiCr10)

Classification

Country Section Category
Germany Structural, Pressure Vessel and Engineering Steels Cr-Ni with Cr < 1.0%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, %
95.01–96.55 0.15–0.35 0.4–0.7 0.55–0.95 2.25–2.75 < 0.035 0.1–0.17 < 0.035

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ $$\epsilon_L$$, % $$\psi$$, % $$KU$$, $$J$$ Treatment
< 11 980–1270 > 735 > 9 > 40 > 69 After carburization, in the core
< 30 880–1180 > 685 > 11 > 45 > 69 Cementation, in the core
< 63 830–1080 > 685 > 11 > 45 Cementation, in the core

Brinell hardness number

Rolling Standard Classifiers Value, HBW
soft, average vacation < 205

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\psi$$ % Reduction in cross section on fracture
$$KU$$ $$J$$ Impact energy