1.6510

Classification

Country Section Category
Germany Structural, Pressure Vessel and Engineering Steels Cr-Ni-Mo with Mo < 0.4% + Ni < 0.2%

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % P, % C, % S, % Mo, %
96.06–97.7 < 0.4 0.5–0.8 0.6–1 0.7–1 < 0.025 0.35–0.43 < 0.035 0.15–0.25

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$, % $$R_{eH}$$, $$MPa$$ $$\psi$$, % Treatment
< 16 moderate hardening 980–1180 11 785 40
16–40 moderate hardening 930–1130 11 735 40
40–100 moderate hardening 880–1080 12 685 45
100–160 moderate hardening 830–980 12 635 50
160–250 moderate hardening 740–880 13 540 50

Brinell hardness number

Rolling Standard Classifiers Value, HBW
annealing, soft 240

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ % Elongation at break (longitudinal) (for L0 = 5.65√So)
$$R_{eH}$$ $$MPa$$ Upper yield point
$$\psi$$ % Reduction in cross section on fracture