1.6932 (28NiCrMoV8-5)
Classification
| Country |
Section |
Category |
| Germany |
Structural, Pressure Vessel and Engineering Steels |
Cr-Ni except Groups 57 to 68 |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
V, % |
P, % |
C, % |
S, % |
Mo, % |
|---|
|
94.51–96.41 |
< 0.4 |
0.15–0.4 |
1–1.5 |
1.8–2.1 |
0.05–0.15 |
< 0.035 |
0.24–0.32 |
< 0.035 |
0.35–0.55 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\epsilon_T$$, % |
$$R_{eH}$$, $$MPa$$ |
Treatment |
|---|
|
|
< 160 |
|
moderate hardening |
800 |
14 |
10–11 |
630 |
|
|
|
160–330 |
|
moderate hardening |
750 |
15 |
|
590 |
|
|
|
330–660 |
|
moderate hardening |
750 |
15 |
|
590 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
|
|
soft, annealing |
< 248 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| V |
% |
Vanadium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Mo |
% |
Molybdenum |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\epsilon_T$$ |
% |
Elongation at break (transverse) |
| $$R_{eH}$$ |
$$MPa$$ |
Upper yield point |