1.7379 (G17CrMo9-10)

Country	Section	Category
Country	Section	Category
Germany	Structural, Pressure Vessel and Engineering Steels	Cr-Mo with Mo ≥ 0.35%

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	V, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	V, %	P, %	C, %	S, %	Mo, %
	93.81–96.47	< 0.6	0.5–0.9	2–2.5	< 0.3	< 0.4	< 0.05	< 0.02	0.13–0.2	< 0.02	0.9–1.2

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$KV_{L}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$KV_{L}$ , $J$	Treatment
				moderate hardening	590–740	400	18	40

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$KV_{L}$	$J$	Impact energy (longitudinal)