1.7383 (11CrMo9-10)
Classification
| Country |
Section |
Category |
| Germany |
Structural, Pressure Vessel and Engineering Steels |
Cr-Mo with Mo ≥ 0.35% |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
P, % |
C, % |
S, % |
Mo, % |
|---|
|
94.91–96.62 |
< 0.5 |
0.4–0.8 |
2–2.5 |
< 0.025 |
0.08–0.15 |
< 0.015 |
0.9–1.1 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{Y}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\epsilon_T$$, % |
$$KV_{L}$$, $$J$$ |
$$KV_{T}$$, $$J$$ |
Treatment |
|---|
|
|
|
|
moderate hardening |
540–680 |
355 |
|
|
|
|
|
|
|
< 200 |
|
Hardening, normalization |
520–670 |
310 |
20 |
20 |
|
|
|
|
|
200–500 |
|
Hardening, normalization |
450–600 |
265 |
23 |
21 |
|
|
|
|
|
|
|
Hardening, Quenching in water |
520–670 |
310 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
40–60 |
27–50 |
|
|
|
< 60 |
|
Hardening, Quenching in water |
|
|
18 |
|
|
|
|
|
|
60–100 |
|
Hardening, Quenching in water |
|
|
17 |
|
|
|
|
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Mo |
% |
Molybdenum |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{Y}$$ |
$$MPa$$ |
Yield strength |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\epsilon_T$$ |
% |
Elongation at break (transverse) |
| $$KV_{L}$$ |
$$J$$ |
Impact energy (longitudinal) |
| $$KV_{T}$$ |
$$J$$ |
Impact energy (transverse) |