07H18N10G2S2M2L

for producing castings for various industrial applications. Steel austenitic-ferritic class.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Steels and alloys for castings	Ordinary steel for castings

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	Mo, %
GOST 977-88	62.35–72	< 2	< 2	17–19	9–12	< 0.04	< 0.07	< 0.04	2–2.5

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	d5, %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	d5, %	Treatment
Castings	GOST 977-88				432	177	35	441	30	Hardening 1050 - 1100 ° C, cooling in water or in air

Heat Treatment Modes

Treatment
Treatment
Hardening 1050 - 1100 ° C, cooling in water or in air

Analogues

Germany	USA
Germany	USA
F 1.4408	CF8M

Standards

Standard	Description
Standard	Description
GOST 977-88

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Mo	%	Molybdenum

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
d5	%	Elongation at break
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness