10G2S1

The steel alloyed is silicon-manganic, not prone to temper brittleness. Weldability without restrictions. Flock sensitivity: not sensitive.

Drums of boilers, vessels, working under pressure, and other parts of boilers operating at temperatures up to 450 degrees.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Low alloy structural steel for welded structures

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % As, % P, % C, % S, % N, %
GOST 19281-89 96.067–97.9 0.8–1.1 1.3–1.65 < 0.3 < 0.3 < 0.3 < 0.08 < 0.035 < 0.12 < 0.04 < 0.008

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ Treatment
Sheet GOST 5520-79 430–490 295–355 21 590–640
Grade GOST 19281-2014 < 140 480 345 21

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
no limits not sensitive not inclined

Critical point temperatures

Ac1, K Ac3(Acm), K Ar3(Arcm), K Ar1, K
763–745 920–927 790–820 640–735
10G2S1 / Aloro

Standards

Standard Description
GOST 19281-89

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
As % Arsenic
P % Phosphorus
C % Carbon
S % Sulfur
N % Nitrogen

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$KCU\cdot 10^{3}$$ $$\frac{J}{m^2}$$ Impact toughness

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter Units of measurement Description
Ac1 K
Ac3(Acm) K
Ar3(Arcm) K
Ar1 K