10G2S1D

Structural alloyed silicon-manganic steel with copper for welded structures.

For welded structures

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Structural steel	Low alloy structural steel for welded structures

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	As, %	P, %	C, %	S, %	N, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	As, %	P, %	C, %	S, %	N, %
GOST 19281-89	96.063–97.75	0.8–1.1	1.3–1.65	< 0.3	0.15–0.3	< 0.3	< 0.08	< 0.035	< 0.12	< 0.04	< 0.012

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Sheet	GOST 19282-73	5–9			500	350	21	650
Grade	GOST 19281-2014	< 140			480	345	21

Technological Properties

Weldability
Weldability
no limits

Standards

Standard	Description
Standard	Description
GOST 19281-89

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
As	%	Arsenic
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures